BOPLA Bio-Degradable Film

Cat. No.	Specification	Price
LC01503736-01	ECPs Composite Type (Thickness: 15/25/40μm, Width: 300-2100mm, Single/Double Sided Corona, Single/Double Side Heat Sealing)	Inquiry
LC01503736-02	ESL Heat Seal Type (Thickness: 15/25/40μm, Width: 300-2100mm, Single/Double Sided Corona, Single/Double Side Heat Sealing)	Inquiry
LC01503736-03	ECP Standard Type Thickness: 15/25/28/40μm, Width: 300-2100mm, Single/Double Sided Corona)	Inquiry

Add to Cart

Product Description

Product Description

BOPLA, a new biodegradable film that is the first to realize large-scale production, is a revolutionary green scientific and technological product through multi-dimensional innovation such as formula research, film structure design and process technology. It is also an important material to accelerate the realization of the national carbon peak and carbon neutralization strategic goals. It can widely replace the disposable film that used in logistics, fresh packaging, paper plastic film and other fields.

Features

· Using polylactic acid as raw material, it has good biocompatibility and degradation performance, and is environmental friendly
· Excellent transparency and gloss, lower haze, excellent printing performance
· Good heat sealing performance, can be directly heat sealing without glue
· Excellent processing performance, good folding form stability and kink retention

Specifications

Product thickness
Typical value: 25μm
Density
Typical value: 1.24g/cm³
Tensile strength MD/TD
Typical value: 135/130MPa
Elongation at break MD/TD
Typical value: 115/125%
Heat shrinkage (100°C, 10min) MD/TD
Typical value: ≤4.5/≤1.5%
Dynamic friction coefficient
Typical value: 0.5
Surface tension, (single-sided corona) treated surface/untreated surface
Typical value: 42/35mN/m
Heat seal strength
Typical value: ≥3.5N/15mm
Test standard: 135kpa/85°C/2S
Haze
Typical value: ≤1.5%
Gloss (45°)
Typical value: ≥85%
Transmittance
Typical value: ≥90%

Applications

Application Description

The biaxial stretching process can greatly improve the mechanical properties of PLA film, and further expand its application fields. It can be used in tape, food packaging, fresh packaging, paper laminating and other fields, which is of great significance for packaging reduction, environmental protection and carbon reduction.